稀土元素增强铝合金作为一种适用于选区激光熔化(selective laser melting, SLM)工艺的合金,由于其良好的成形质量和优越的力学性能而得到了广泛应用。但其成形质量由成形参数决定。通过控制激光功率、扫描速度、扫描间距等关键工艺参数的变化,研究了关键工艺参数的变化对选区激光熔化稀土元素增强铝合金的致密度、缺陷类型演变的影响。结果表明,工艺参数的变化会导致能量密度的变化,合金致密度由体能量密度和线能量密度共同影响,当体能量密度在70～180 J/mm3且线能量密度为0.250～0.525 J/mm时,合金致密度能够稳定在99.5%以上。
Abstract：As an alloy suitable for selective laser melting(SLM) process, rare earth elements doped aluminum alloy has been widely used due to its superior mechanical properties and good formability. The forming quality is determined by the processing parameters. In this paper, by controlling key process parameters such as laser power, scanning velocity and hatch spacing, the evolution of relative density and defect types of SLM rare earth elements doped aluminum alloys at different process parameters are studied. The results show that changes in process parameters will lead to changes in energy density, the relative density of the alloy is affected by the volumetric energy density and the liner energy density of the single pass. When the volumetric energy density is 70-180 J/mm3 and the liner energy density is 0.250-0.525 J/mm, the relative density of the alloy is stable above 99.5%.
[1] 顾冬冬，张红梅，陈洪宇，等.航空航天高性能金属材料构件激光增材制造[J].中国激光，2020,47(5):0500002.
[2] PONNUSAMY P,RASHID R A R,MASOOD S H,et al.Mechanicalproperties of SLM-printed aluminium alloys:A review[J].Materials,2020,13(19):4301.
[3] ABOULKHAIR N T,SIMONELLI M,PARRY L,et al.3D printing of aluminium alloys:Additive manufacturing of aluminium alloys using selective laser melting[J].Progress in Materials Science,2019,106:100578.
[4] GU D D,CHANG F,DAI D H.Selective laser melting additive manufacturing of novel aluminum based composites with multiple reinforcing phases[J].Journal of Manufacturing Science and Engineering,2015,137(2):021010.
[5] XU W,BRANDT M,SUN S,et al.Additive manufacturing of strong and ductile Ti6Al4V by selective laser melting via in situ martensite decomposition[J].Acta Materialia,2015,85:74-84.
[6] VILARO T,COLIN C,BARTOUT J D.As-fabricated and heat-treated microstructures of the Ti6Al4V alloy processed by selective laser melting[J].Metallurgical and Materials Transactions A,2011,42(10):3190-3199.
[7] SIMONELLI M,TSE Y Y,TUCK C.Effect of the build orientation on the mechanical properties and fracture modes of SLM Ti6Al4V[J].Materials Science and Engineering:A,2014,616:1-11.
[8] 潘纬韬，祝国梁，王瑞，等.固溶和时效处理对选区激光熔化成形GTD222镍基合金组织和硬度的影响[J].机械工程材料，2020,44(11):66-71.
[9] JIA Q B,ZHANG F,ROMETSCH P,et al.Precipitation kinetics,microstructure evolution and mechanical behavior of a developed Al-Mn-Sc alloy fabricated by selective laser melting[J].Acta Materialia,2020,193:239-251.
[10] OLAKANMI E O,COCHRANE R F,DALGARNO K W.A review on selective laser sintering/melting (SLS/SLM) of aluminium alloy powders:Processing,microstructure,and properties[J].Progress in Materials Science,2015,74:401-477.
[11] MARTIN J H,YAHATA B D,HUNDLEY J M,et al.3D printing of high-strength aluminium alloys[J].Nature,2017,549:365-369.
[12] AWD M,TENKAMP J,HIRTLER M,et al.Comparison of microstructure and mechanical properties of scalmalloy? produced by selective laser melting and laser metal deposition[J].Materials,2017,11(1):17.
[13] JIA Q B,ROMETSCH P,KüRNSTEINER P,et al.Selective laser melting of a high strength AlMnSc alloy:Alloy design and strengthening mechanisms[J].Acta Materialia,2019,171:108-118.
[14] LI R D,WANG M B,LI Z M,et al.Developing a high-strength Al-Mg-Si-Sc-Zr alloy for selective laser melting:Crack-inhibiting and multiple strengthening mechanisms[J].Acta Materialia,2020,193:83-98.
[15] MA R L,PENG C Q,CAI Z Y,et al.Effect of bimodal microstructure on the tensile properties of selective laser melt Al-Mg-Sc-Zr alloy[J].Journal of Alloys and Compounds,2020,815:152422.
[16] WANG M B,LI R D,YUAN T C,et al.Microstructures and mechanical property ofAlMgScZrMn:A comparison between selective laser melting,spark plasma sintering and cast[J].Materials Science and Engineering:A,2019,756:354-364.
[17] SPIERINGS A B,DAWSON K,KERN K,et al.SLM-processed Sc-and Zr-modified Al-Mg alloy:Mechanical properties and microstructural effects of heat treatment[J].Materials Science and Engineering:A,2017,701:264-273.
[18] 张书雅.形核剂对增材制造铝合金显微组织及力学性能的影响[D].济南：山东大学，2020:11-12.
[19] NORMAN A F,PRANGNELL P B,MCEWEN R S.The solidification behaviour of dilute aluminium-scandium alloys[J].Acta Materialia,1998,46(16):5715-5732.
[20] VENKATESWARLU K,RAJINIKANTH V,RAY A K,et al.The characteristics of aluminum-scandium alloys processed by ECAP[J].Materials Science and Engineering:A,2010,527(6):1448-1452.
[21] ZHANG H,GU D D,DAI D H,et al.Influence of scanning strategy and parameter on microstructural feature,residual stress and performance of Sc and Zr modified Al-Mg alloy produced by selective laser melting[J].Materials Science and Engineering:A,2020,788:139593.
[22] WANG D,DOU W H,YANG Y Q.Research on selective laser melting of Ti6Al4V:surface morphologies,optimized processing zone,and ductility improvement mechanism[J].Metals,2018,8(7):471.
[23] PAL S,LOJEN G,KOKOL V,et al.Evolution of metallurgical properties of Ti6Al4V alloy fabricated in different energy densities in the Selective Laser Melting technique[J].Journal of Manufacturing Processes,2018,35:538-546.
[24] ZHAO C,PARAB N D,LI X X,et al.Critical instability at moving keyhole tip generates porosity in laser melting[J].Science,2020,370:1080-1086.
[25] CAO S,CHEN Z E,LIM C V S,et al.Defect,microstructure,and mechanical property of Ti6Al4V alloy fabricated by high-power selective laser melting[J].JOM,2017,69(12):2684-2692.
[26] GU D D,MEINERS W,WISSENBACH K,et al.Laser additive manufacturing of metallic components:materials,processes and mechanisms[J].International Materials Reviews,2012,57(3):133-164.
基本信息:
DOI：10.14128/j.cnki.al.20214106.1229
中图分类号:TG665;TG146.21
引用信息:
[1]任治倪,徐迪,黄洁,等.关键工艺参数对选区激光熔化稀土元素增强铝合金成形致密度的影响[J].应用激光,2021,41(06):1229-1236.DOI:10.14128/j.cnki.al.20214106.1229.
基金信息:
国家重点研发计划(2018YFB1106300)
2021-03-17
2021
2021-03-30
2021
1
2021-12-25
2021-12-25