针对选区激光熔化单层316L,采用ABAQUS软件,利用DFLUX子程序编译移动双椭球热源并结合USDFLD子程序实现材料属性转变的方法数值模拟SLM过程,考虑了材料由粉体转化为实体的热物性参数和相变潜热对SLM的影响,分析了单层扫描过程中温度场的变化规律,包括扫描轨道中点的温度变化、熔池存在时间以及熔池结构。研究结果发现,随着扫描轨道逐渐增加,扫描轨道中点的峰值温度、熔池存在时间及熔池结构在初始阶段增幅较大,之后变得相对平缓并达到稳定状态。表明在SLM过程中,随着扫描轨道增加,扫描区域的温度场会逐渐处于动态稳定状态。
Abstract：The process of selective laser melting single layer 316 Lis studied.The DFLUX subroutine to compile the moving double ellipsoid heat source and the USDFLD subroutine to change the material properties in ABAQUS software to numerically simulate SLM process.The influence of thermal physical properties parameters of material from the powder into the solid and the latent heat of phase change on SLM are considered.The temperature field variation during single layer scanning is analyzed,including the temperature change at the midpoint of the scanning track,the molten pool lifetime and the molten pool dimension.The results show that as the scanning track gradually increases,the peak temperature at the midpoint of the scanning track,the molten pool lifetime and the molten pool dimension increase greatly in the initial stage,and then become relatively flat and reach a stable state.Indicating that during the SLM process,with the scanning track increases,the temperature field of the scanning area will gradually be in a dynamic stable state.
[1]LU BINGHENG,LI DICHEN.Development of the additive manufacturing(3D printing)technology[J].Machine Building&Automation,2013,42(4):1-4.卢秉恒,李涤尘.增材制造(3D打印)技术发展[J].机械制造与自动化,2013,42(4):1-4.
[2]LI DICHEN,TIAN XIAOYONG,WANG YONGXIN,et al.Developments of Additive Manufacturing Technology[J].Electromachining&Mould,2012(s1):20-22.李涤尘,田小永,王永信,等.增材制造技术的发展[J].电加工与模具,2012(s1):20-22.
[3]LIN XIN,HUANG WEIDONG.Laser additive manufacturing of high-performance metal components[J].Science China,2015,45(9):1111-1126.林鑫,黄卫东.高性能金属构件的激光增材制造[J].中国科学:信息科学,2015,45(9):1111-1126.
[4]DONG L,MAKRADI A,AHZI S,et al.Three-dimensional transient finite element analysis of the selective laser sintering process[J].Journal of Materials Processing Technology,2009,209(2):700-706.
[5]SHEN XIANFENG,WANG YANG,YAO JIN,et al.Finite element simulation of thermal distribution in direct metal laser multi-track sintering[J].Advanced Engineering Sciences,2005,37(1):47-51.沈显峰,王洋,姚进,等.直接金属选区激光多道烧结温度场有限元模拟[J].四川大学学报(工程科学版),2005,37(1):47-51.
[6]SHI QIMING,GU DONGDONG,XIA MUJIAN,et al.Effects of laser processing parameters on thermal behavior and melting/solidification mechanism during selective laser melting of TiC/Inconel 718composites[J].Optics&Laser Technology,2016(84):9-22.
[7]ZHAO HAILING.Numerical simulation of temperature field and flow field during laser cladding of molten pool[D].Qinhuangdao:Yanshan university,2013.赵海玲.激光熔覆熔池温度场和流场的数值模拟[D].秦皇岛:燕山大学,2013.
[8]CHUKKAN J R,VASUDEVAN M,MUTHUKUMARAN S,et al.Simulation of laser butt welding of AISI316Lstainless steel sheet using various heat sources and experimental validation[J].Journal of Materials Processing Technology,2015(219):48-59.
[9]THUMMLER F,OBERACKER R.An introduction to powder metallurgy[M].The Institute of Materials,1993.
[10]JIANG XIANFENG,MENG XIANGCHEN,SONG RONGWEI,et al.Study on the effects of temperature field of material state change in the SLM process[J].Applied Laser,2015,35(2):155-159.姜献峰,孟祥陈,宋荣伟,等.SLM加工中材料状态变化对温度场影响的研究[J].应用激光,2015(2):155-159.
基本信息:
DOI：10.14128/j.cnki.al.20183805.748
中图分类号:TG665
引用信息:
[1]段成红,郝晓杰,罗翔鹏.选区激光熔化316L温度场研究[J].应用激光,2018,38(05):748-753.DOI:10.14128/j.cnki.al.20183805.748.
基金信息:
国家重点研发计划资助项目(项目编号:2016YFB1100202)
2018-10-15
2018-10-15